Mesoscopic patterning in evaporated polymer solutions: Poly(ethylene glycol) and room-temperature-vulcanized polyorganosilanes/-siloxanes promote formation of honeycomb structures

Edward Bormashenko, Alexander Malkin, Albina Musin, Yelena Bormashenko, Gene Whyman, Natalya Litvak, Zahava Barkay, Vladimir Machavariani

פרסום מחקרי: פרסום בכתב עתמאמרביקורת עמיתים

38 ציטוטים ‏(Scopus)

תקציר

Patterning in evaporated polymer solutions based on amorphous polymers and chlorinated solvents has been investigated. Bilayered films patterned on two scales, i.e., 50 and 5 m, are obtained. The addition of polyorganosilane/- siloxane to solutions destroys the large-scale pattern. Polyethylene glycol) promotes the formation of more dense close-packed structures on the mesoscopic scale (≈5 m). Short-range and mesoscopic (liquid-like) ordering of the honeycomb structures on the characteristic scale of 5 m is revealed with the statistical analysis of SEM images. Physical mechanisms responsible for patterning are discussed.

שפה מקוריתאנגלית
עמודים (מ-עד)567-576
מספר עמודים10
כתב עתMacromolecular Chemistry and Physics
כרך209
מספר גיליון6
מזהי עצם דיגיטלי (DOIs)
סטטוס פרסוםפורסם - 25 מרץ 2008

טביעת אצבע

להלן מוצגים תחומי המחקר של הפרסום 'Mesoscopic patterning in evaporated polymer solutions: Poly(ethylene glycol) and room-temperature-vulcanized polyorganosilanes/-siloxanes promote formation of honeycomb structures'. יחד הם יוצרים טביעת אצבע ייחודית.

פורמט ציטוט ביבליוגרפי