TY - JOUR
T1 - The characterization and quantification of the induced mesophases of poly-l-lactic acid
AU - Baptista, Cameron
AU - Azagury, Aharon
AU - Baker, Christopher M.
AU - Mathiowitz, Edith
N1 - Publisher Copyright:
© 2021 Elsevier Ltd
PY - 2021/6/4
Y1 - 2021/6/4
N2 - The pressure-temperature induced mesophases of poly-L-lactic acid (PLA) were studied upon processing at 20,000 lbf, for 15 min, at varying temperatures from 40 to 120 °C. The morphology and melting behavior of the processed samples were analyzed by x-ray diffraction (XRD), polarized light microscopy (PLM), and differential scanning calorimetry (DSC). Samples processed near and below the glass transition temperature at 52 °C and 63 °C displayed a nematic-like mesophase, characterized by orientational order of the amorphous XRD scattering, birefringence by PLM, and a post-Tg endotherm by DSC. The nematic-like mesophase quantity in these samples was determined to be 8.7%–20.5%, respectively, based on hot-stage XRD and peak deconvolution. This nematic-like state was shown to disorder upon heating around the glass transition at 65 °C. Samples processing above the glass transition temperature at 74 °C, 85 °C, and 120 °C, displayed a condis crystal-like mesophase, characterized by crystalline reflections of the mesophase XRD scattering, birefringence by PLM, and an increased melting endotherm by DSC. The total quantity of mesophase in these samples was shown to be betweeen 8.8% and 15.8%. Thus, this paper reports the characterization and quantification of two distinct PLA mesophases upon pressure-temperature processing: a nematic-like mesophase formed at temperatures below the glass transition and a condis crystal-like mesophase formed at temperatures above the glass transition.
AB - The pressure-temperature induced mesophases of poly-L-lactic acid (PLA) were studied upon processing at 20,000 lbf, for 15 min, at varying temperatures from 40 to 120 °C. The morphology and melting behavior of the processed samples were analyzed by x-ray diffraction (XRD), polarized light microscopy (PLM), and differential scanning calorimetry (DSC). Samples processed near and below the glass transition temperature at 52 °C and 63 °C displayed a nematic-like mesophase, characterized by orientational order of the amorphous XRD scattering, birefringence by PLM, and a post-Tg endotherm by DSC. The nematic-like mesophase quantity in these samples was determined to be 8.7%–20.5%, respectively, based on hot-stage XRD and peak deconvolution. This nematic-like state was shown to disorder upon heating around the glass transition at 65 °C. Samples processing above the glass transition temperature at 74 °C, 85 °C, and 120 °C, displayed a condis crystal-like mesophase, characterized by crystalline reflections of the mesophase XRD scattering, birefringence by PLM, and an increased melting endotherm by DSC. The total quantity of mesophase in these samples was shown to be betweeen 8.8% and 15.8%. Thus, this paper reports the characterization and quantification of two distinct PLA mesophases upon pressure-temperature processing: a nematic-like mesophase formed at temperatures below the glass transition and a condis crystal-like mesophase formed at temperatures above the glass transition.
KW - Biopolymers
KW - Mesophase
KW - Polylactic acid
UR - http://www.scopus.com/inward/record.url?scp=85105570553&partnerID=8YFLogxK
U2 - 10.1016/j.polymer.2021.123822
DO - 10.1016/j.polymer.2021.123822
M3 - ???researchoutput.researchoutputtypes.contributiontojournal.article???
AN - SCOPUS:85105570553
SN - 0032-3861
VL - 226
JO - Polymer
JF - Polymer
M1 - 123822
ER -