EDTA incorporated Fe-Zn double metal cyanide catalyst for the controlled synthesis of polyoxypropylene glycol

Akash Verma, Swati Saini, Bhawna Sharma, Vikas Verma, Babita Behera, Raghuvir Singh, Sudip K. Ganguly, Anjan Ray, Alexander Vorontsov, Umesh Kumar

نتاج البحث: نشر في مجلةمقالةمراجعة النظراء

9 اقتباسات (Scopus)

ملخص

One pot, solvent free ring opening polymerization (ROP) of propylene oxide (PO) was studied by using lab synthesized heterogeneous double metal cyanide (DMC) catalyst. A series of DMC catalysts was prepared by using EDTA as novel complexing agent (CA) and characterized in detail by PXRD, FT-IR, UV–Vis, 13C CP-MAS NMR, AAS, SEM, XPS, and CHNS analyzer. The suitable amount of CA favored high Zn/Fe ratio and enhanced catalytic activity for polyoxypropylene glycol (PPG) synthesis. It was observed that the properties of PPG are governed by reaction parameters, including catalyst amount, reaction time, temperature, pressure, feed to initiator ratio, and different initiators. The prepared polymers have Mw (160 to 19,667 g mol−1) and PDI (1.05 to 3.01) during optimization. The structure elucidation of PPG was confirmed by FT-IR, GPC, and 1H NMR. Dipropylene glycol (DPG) initiator yielded highest 93% PPG with 1.29 PDI, and 4.9 mg-KOH g−1 hydroxyl value. The kinetics study confirms first-order reaction with proposed coordination mechanism.[Figure not available: see fulltext.]

اللغة الأصليةالإنجليزيّة
رقم المقال62
دوريةJournal of Polymer Research
مستوى الصوت30
رقم الإصدار2
المعرِّفات الرقمية للأشياء
حالة النشرنُشِر - فبراير 2023

بصمة

أدرس بدقة موضوعات البحث “EDTA incorporated Fe-Zn double metal cyanide catalyst for the controlled synthesis of polyoxypropylene glycol'. فهما يشكلان معًا بصمة فريدة.

قم بذكر هذا